High Performance of Superconducting YBa2Cu3O7 Thick Films Prepared by Single-Deposition Inkjet Printing
23 November 2021
Inkjet printing (IJP) is a very appealing cost-effective deposition technique to achieve large-area solution-derived functional films. For many applications, it is very challenging to increase the film thickness in order to achieve competitive performance, for instance, high critical currents in superconducting films. In this paper, the preparation of superconducting YBa2Cu3O7 thick films (∼1.1 μm) using a single deposition is reported. Specific rules for ink design, deposition protocols, and pyrolysis processes are provided.
The most important aspect is to formulate an ink with a solvent having a high boiling point that keeps the whole film wet during deposition to avoid liquid movement due to coffee-ring effects. An additional success has been to modify the ink with a photocurable polyacrylic ester varnish which after polymerization with a UV LED lamp helps keep homogeneous thickness. This varnish also helped avoid the generation of film instabilities (wrinkling or cracking) during pyrolysis. Homogeneous pyrolyzed thick films are transformed into epitaxial thick films with high critical currents. The IJP process is shown to be valid to prepare nanocomposite films using colloidal inks including pre-prepared BaZrO3 nanoparticles. The nanocomposite thick films display enhanced vortex pinning, thus keeping high critical currents under high magnetic fields.
Hits: 1320
M4NRG Clean Energy

High Performance of Superconducting YBa2Cu3O7 Thick Films Prepared by Single-Deposition Inkjet Printing

Bohores Villarejo, Flavio Pino, Cornelia Pop, Susagna Ricart, Ferran Vallès, Bernat Mundet, Anna Palau, Pere Roura-Grabulosa, Jordi Farjas, Natalia Chamorro, Ramón Yáñez, Xavier Granados, Teresa Puig*, and Xavier Obradors*

ACS Appl. Electron. Mater. 2021, 3, 9, 3948–3961
Publication Date:August 20, 2021