Optical Analysis of Oxygen Self‐Diffusion in Ultrathin CeO2 Layers at Low Temperatures

Optical Analysis of Oxygen Self‐Diffusion in Ultrathin CeO2 Layers at Low Temperatures

Scientific Highlights Methodologies for materials science and nanotechnology 19 October 2018 259 hits jags
Paula NeuderthPascal HilleSara Martí‐SánchezMaría de la MataMariona CollJordi ArbiolMartin Eickhoff. Advanced Energy Materials 29 August 2018  https://doi.org/10.1002/aenm.201802120
An optical in situ strategy for the analysis of oxygen diffusion in ultrathin ceria layers with a thickness of 2–10 nm at temperatures between 50 and 200 °C is presented, which allows for the determination of diffusion coefficients. This method is based on the sensitivity of the photoluminescence (PL) intensity of InGaN nanowires to adsorbed oxygen. The oxygen diffusion through an ultrathin CeO2 coating deposited on the InGaN nanowires is monitored by analyzing the transient PL behavior of the InGaN nanowires, which responds to changes of the oxygen concentration in the environment when the corresponding oxygen concentration is established at the CeO2/InGaN interface due to diffusion through the coating. Quantitative evaluation of the oxygen diffusion in CeO2based on a model considering Langmuir Adsorption and recombination yields a diffusion coefficient D of (2.55 ± 0.05) × 10−16 cm2 s−1 at a temperature of 100 °C. Temperature‐dependent measurements reveal an Arrhenius type behavior of D with an activation energy of (0.28 ± 0.04) eV. In contrast, no oxygen diffusion is detected for an ultrathin layer (≥5 nm) of Al2O3, which is known as a poor oxygen ion conductor within the analyzed temperature regime.

Related Topics: Methodologies for materials science and nanotechnology

Also on ICMAB...


Your experience on this site will be improved by allowing cookies Cookie Settings